AL₂O₃-SIC-C BRICK
Wear resistance, anti-penetration, slag resistance, long service life
Al₂O₃-SiC-C Brick
Excellent Slag Resistance
Effectively resists erosion from molten iron and slag, reducing penetration.
High Wear Resistance
Withstands erosion from hot gases and molten iron, reducing lining loss.
Thermal Shock Resistance
Withstands frequent temperature fluctuations, reducing cracking risks.
| Brand | ZTM-ASC-T18A | ZTM-ASC-T18B | ZTM-ASC-T20A | ZTM-ASC-T20B |
| Al2O3 (%) | ≥65 | ≥65 | ≥65 | ≥60 |
| SiC+C (%) | ≥18 | ≥18 | ≥20 | ≥20 |
| Bulk Density (g.cm³) | ≥2.85 (200℃, 24h) | ≥2.75 (200℃, 24h) | ≥2.85 (200℃, 24h) | ≥2.80 (200℃, 24h) |
| Apparent Porosity (%) | ≤10 (200℃, 24h) | ≤10 (200℃, 24h) | ≤10 (200℃, 24h) | ≤10 (200℃, 24h) |
| Cold Crushing Strength (MPa) | ≥50 (200℃, 24h) | ≥40 (200℃, 24h) | ≥40 (200℃, 24h) | ≥40 (200℃, 24h) |
| Permanent Linear Change (%) | 0～+1.0 (1400℃, 3h) | 0～+1.0 (1400℃, 3h) | 0～+1.0 (1400℃, 3h) | 0～+1.0 (1400℃, 3h) |
| Application | Side Wall | Top | Impact Area | Slag Line |
long service life
Let our technical experts help you find the perfect Al₂O₃-SiC-C Brick solution.
Contact us today for a customized quote!
Customized Al₂O₃-SiC-C Brick
- Customized Formulation: Tailored to hot metal composition, slag characteristics, and operating temperature.
- Customized Dimensions: Tailored brick sizes and shapes to fit torpedo car structure.